3 Search Results

This paper reports the rational fabrication and structural, thermal, mechanical and electrochemical characterization of a new type of intermediate-temperature (IT) polymer-inorganic composite (PIC) proton exchange membranes (PEMs) that are made of cerium ultraphosphate (CeP₅O₁₄—CUP) as the solid-state proton conductor composited with a high-temperature (HT) polybenzimidazole (PBI) as the polymeric binder. Here, flexible PBI-CUP PIC membranes with the thickness of ~135 μm and CUP mass fraction of up to 75% were prepared by solution-casting without additional acid-doping (e.g., phosphoric acid). The proton conductivity of the fabricated IT-PIC-PEMs was up to 5.80 × 10^–2 S cm^–1 as measured from a prototype ITmore » PEM fuel cell (PEMFC) operated at 200 °C in the humidified hydrogen and air environment. This type of IT-PIC-PEMs also demonstrated sufficient mechanical strength and flexibility, excellent thermal stability (up to 350 °C), and very good durability of the proton conductivity (within the test duration of 500 h). The present experimental study shows the promising future of the IT-PIC-PEMs for applications in various IT electrochemical processes including IT-PEMFCs, IT-electrolyzers, etc.« less

Polymer electrolyte membrane fuel cells (PEMFCs) expect a promising future in addressing the major problems associated with production and consumption of renewable energies and meeting the future societal and environmental needs. Design and fabrication of new proton exchange membranes (PEMs) with high proton conductivity and durability is crucial to overcome the drawbacks of the present PEMs. Acid-doped polybenzimidazoles (PBIs) carry high proton conductivity and long-term thermal, chemical, and structural stabilities are recognized as the suited polymeric materials for next-generation PEMs of high-temperature fuel cells in place of Nafion® membranes. This paper aims to review the recent developments in acid-doped PBI-basedmore » PEMs for use in PEMFCs. The structures and proton conductivity of a variety of acid-doped PBI-based PEMs are discussed. More recent development in PBI-based electrospun nanofiber PEMs is also considered. The electrochemical performance of PBI-based PEMs in PEMFCs and new trends in the optimization of acid-doped PBIs are explored.« less

This article reports a comparative experimental study of the hygroscopic and mechanical behaviors of electrospun polybenzimidazole (PBI) nanofiber membranes and solution-cast PBI films. As-electrospun nonwoven PBI nanofiber mats (with the nanofiber diameter of ~250 nm) were heat-pressed under controlled temperature, pressure and duration for the study; lab-made solution-cast PBI films and commercially available PBI films (the PBI Performance Product Inc., Charlotte, NC) were used as the control samples. Thermogravimetric and microtensile tests were utilized to characterize the hygroscopic (moisture absorption) and mechanical properties of the PBI nanofiber membranes at varying heat-pressing conditions, which were further compared to those of solution-castmore » PBI films. Experimental results indicated that the PBI nanofiber membranes carried slightly higher thermal stability and less hygroscopic properties than those of solution-cast PBI films. In addition, heat-pressing conditions significantly influenced the mechanical properties of the resulting PBI nanofiber membranes. The stiffness and tensile strength increase with increasing either the heat-pressing pressure or duration, and relevant mechanisms were explored. Here, the present study provides a rational understanding of the hygroscopic and mechanical behaviors of electrospun PBI nanofiber membranes and solution-cast PBI films that are beneficial to their reliable cutting-edge applications in high-temperature filtration, polymer electrolyte membranes (PEMs), etc.« less